ASTM Gradel, JIS Grade, TIA, RMI 25, TIMETAL 35A, ST Sheet and plate. ASTM B Gr1, Mil-T CP Bars and billets. ASTM B Gr1. Tube. ASTM B Standard Specification for Titanium and Titanium Alloy Strip, Sheet, and Plate. Amardeep Steel Centre is one of the leader manufacturers, Supplier and exporters of high quality Titanium Plates, Sheets & Coils, Titanium sheets & plates.
|Published (Last):||8 February 2014|
|PDF File Size:||8.71 Mb|
|ePub File Size:||18.87 Mb|
|Price:||Free* [*Free Regsitration Required]|
E The purchaser may, in the written purchase order, request analysis for specic elements not b65 in this specication. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. E For Grades 5, 6 and 32 the elongation on materials under 0.
Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend. Heat numbers shall occur at least 3 times across the width of the sheet and at intervals not greater than 2 ft 0. Committee B10 has identied the location of selected changes to this standard since the last issue B – 09 that may impact the use of this standard.
Bend tests are not applicable to material over 0.
Referee Test and Analysis asm D Other asm need not be reported unless the concentration level is greater than 0. Specied thickness was corrected from 0. NOTE 2—If the longer dimension is under 36 in.
Work Item s – proposed revisions of this standard. The report shall include results of all chemical analysis, tensile tests, and all other tests required by the specication. If you feel that your comments have not received a fair hearing you should make your views known to the ASTM Committee on Standards, at the address shown below.
Aluminum Vanadium Palladium Ruthenium 0. H Material is normally purchased in the solution treated condition. Permissible Variations in Dimensions 7. For plates up to 10 in. The characters shall be sufficiently stable to withstand ordinary handling.
ASTM B _图文_百度文库
Current edition approved May 1, The characters shall be not less than 38 in. ASTM International takes no position respecting the validity of any patent sstm asserted in connection with any item mentioned in this standard.
The frequency of the retest will double the initial number of tests. Only original conforming test results or the conforming retest results shall be reported to the purchaser. In cutting samples for analysis, the operation should be carried out insofar as possible in a dust-free atmosphere because utmost care must be used in sampling titanium for chemical analysis due to its great affinity for elements such as oxygen, nitrogen, and hydrogen.
Lower hydrogen may be obtained by negotiation with the manufacturer. The utmost care must be used in sampling titanium for chemical analysis because of its great affinity for elements such as oxygen, nitrogen, and hydrogen.
In titanium these elements typically include aluminum, vanadium, tin, chromium, molybdenum, niobium, zirconium, hafnium, bismuth, ruthenium, palladium, yttrium, copper, silicon, cobalt, tantalum, nickel, boron, manganese, and tungsten. Grades 2H, 7H, 16H, and 26H are intended primarily for pressure vessel use. NOTE 3—The shorter dimension specied is considered the width and the variation in atness across the width does not exceed the tabular amount for that dimension.
If the results of the retest conform to the specication, then the retest values will become the test values for certication. Surface Requirement Bend Tests S1. This abstract is a brief summary of the referenced standard.
Titanium Plates, Sheets & Coils
B For thicknesses under 0. Permission rights to photocopy the standard may also be secured from the ASTM website www. Link to Active This link will always route to the current Active version of the standard. In titanium these elements include aluminum, vanadium, tin, iron, chromium, molybdenum, niobium, zirconium, hafnium, bismuth, ruthenium, palladium, yttrium, copper, silicon, cobalt, tantalum, nickel, boron, manganese and tungsten.
Final product hydrogen shall be reported.
Ingot hydrogen need not be reported. G Properties for material in the solution treated condition. Tensile properties shall be determined using a strain rate of 0. The grades of titanium and titanium alloy metal covered by this specification shall have the chemical composition requirements of: NOTE 4—The maximum deviation from a at surface does not customarily exceed the tabular tolerance for the longer dimension specied.